Dinamički kontaktni kut u funkciji karakterizacije tiskovnih formi

master's thesis

• Author: Dino Guljelmović
• Mentor: Sanja Mahović Poljaček (mentor)
• Committee member: Sanja Mahović Poljaček (član povjerenstva)
• Granter: University of Zagreb; Faculty of Graphic Arts; Zagreb
• Defense date and country: 2009-10-00, Croatia
• Scientific / art field, discipline and subdiscipline: TECHNICAL SCIENCES; Graphic Technology

Abstract

Dinamički kontaktni kut praćen je na tiskovnim i slobodnim površinama ofsetne tiskovne forme pri čemu su korištene tri kapljevine definirane disperzne i polarne faze (voda, glicerol i dijodometan). Praćene su promjene u kontaktnom kutu s obzirom na volumen i na vrijeme adsorpcije kapljevine.

Dobiveni rezultati ukazuju da se kod vode i glicerola, na slobodnim i na tiskovnim površinama, kontaktni kut smanjuje s vremenom adsorpcije, neovisno o volumenu (bolje močenje površina).

Dinamički kontaktni kut mjeren aplikacijom dijodometana na slobodnim i tiskovnim površine ukazuje da vrijeme adsorpcije minimalno utječe na iznos kontaktnog kuta, budući da je dijodometan izrazito nepolaran i od promatranih kapljevina ima najmanju slobodnu površinsku energiju.

Vrijednost kontaktnog kuta dobivena aplikacijom glicerola na tiskovne i slobodne površine raste, povećanjem volumena kapljevine.

Povećanjem volumena vode na tiskovnim površinama, povećava se i vrijednost kontaktnog kuta, dok kod slobodnih površina vrijednost kontaktnog kuta pada s povećanjem volumena.

Zbog svoje nepolarnosti, kontaktni kut dijodometana na tiskovnim površinama se povećava s povećanjem volumena, dok kod slobodnih površina vrijednost kontaktnog kuta izrazito varira s obzirom na volumen kapi te nije moguće pronaći smjer promjene.

Prema dobivenim rezultatima može se zaključiti da će močenje ovisiti o karakteru i svojstvima površina i kapljevina. Močenje određene površine ovisit će i o pH vrijednosti otopine, napetosti površine, površinski aktivnim tvarima, hrapavosti površine čvrste vari, površinskom naboju te vanjskim čimbenicima (temperatura, vlaga), i slično.

Abstract (english)

Dynamic contact angle was measured on the printing and non‐printing surfaces of the offset printing plate. The measurement was preformed by using three test liquids with defined polar and dispersive components (water, glycerol and diiodomethane). Variations in contact angle values were observed by applying the test liquids of different volume and measured within different adsorption period.

Results have shown that contact angle values have been decreased during the adsorption period on the printing and non‐printing surfaces by using water and glycerol without any influence of liquids’ volume.

Results obtained by application of diiodomethane on the printing and nonprinting areas have shown that adsorption period has minimal influence on the dynamic contact angle values. These results are probably the consequence of diiodomethanes low surface energy values.

By the application of glycerol on the printing and nonprinting areas of the printing plate, contact angle values increase by the application of higher volume values.

Results of the contact angle values obtained by the application of water with different volume on the printing areas have shown higher values, and lower values on the nonprinting areas.

According to the obtained results one can conclude that wetting of the printing plate surfaces depends of the surface characteristics and characteristics of the liquids. Among this, wetting will depend on pH values of the liquids, surface tension, surface active components, surface roughness, surface charge, ambient conditions (temperature, moisture), etc.

• Keywords: Offsetne tiskovne forme; kontaktni kut; močenje; volumen; vrijeme adsorpcije
• Keywords (english): Offset printing plates; dynamic contact angle; wetting; volume; adsorption period
• Language: croatian
• URN:NBN: urn:nbn:hr:216:419304
• Study programme: Title: Graphic technology; specializations in: Graphic technology, Design of graphic products; Course: Graphic technology; Study programme type: university; Study level: graduate; Academic / professional title: sveučilišni/a magistar/magistra inženjer/inženjerka grafičke tehnologije (sveučilišni/a magistar/magistra inženjer/inženjerka grafičke tehnologije)
• Type of resource: Text
• File origin: Born digital
• Access conditions: Closed access
• Created on: 2024-04-17 10:11:53