Devijacije u obojenju otisaka prilikom etiketiranja stezljivim filmom

diplomski rad

• Autor: Bernarda Koletić
• Mentor: Irena Bates (mentor)
• Član povjerenstva: Igor Zjakić (član povjerenstva)
• Član povjerenstva: Irena Bates (član povjerenstva)
• Član povjerenstva: Dubravko Banić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Grafički fakultet; Zagreb
• Datum i država obrane: 2018-9-25, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Grafička tehnologija

Sažetak

Etiketiranja stezljivim filmom je proces apliciranja etikete djelovanjem temperature pri

čemu film oblikovan u rukavac se priljubljuje uz ambalažu i poprima njezin oblik.

Takva vrsta etiketiranja koristi se na različitim ambalažama (polimernim, staklenim ili

metalnim). Etikete korištene kod ove vrste etiketiranja mogu biti u otvorenom formatu

ili formiranje u crijevo (ovisno o liniji za etiketiranje). U ovom radu analizirat će se

uzorci koji su otisnuti fleksografskim tiskom s bojama na bazi otapala i UV sušeće boje.

Analizirani će se uzorci otisnuti na dvije vrste polimernih materijala (polipropilen i

poli(vinil-klorid)). Kako bi se simulirao tunel za etiketiranje stezljivim filmom uzorci će

se izložiti povišenom temperaturom u sušioniku. Uzorci će biti izloženi različitim

temperaturama, ovisno o temperaturi skupljanja tiskovne podloge, odnosno polimernog

materijala. Uzorci otisnuti na polipropilenu izložiti će se temperaturi od 120˚ i 125˚C, a

uzorci otisnuti na poli(vinil-kloridnom) materijalu temperaturi od 70˚ i 75˚C u

jednakom trajanju od 5 minuta. Cilj ovog rada je odrediti devijacije u obojenju otiska na

rastertonskim vrijednostima od 90%, 70% i 20% nakon tretmana s povišenom

temperaturom na osnovi spektrofotometrijskih mjerenja i Euklidske razlike između

boja.

Sažetak (engleski)

The film labeling is the process of applying the label by the effect of temperature,

whereby the film formed in the sleeve is adhered to the packaging and takes its shape.

Such type of labeling is used in different packaging (polymer, glass or metal). The

labels used in this type of labeling can be in the open format or the formation of the

hose (depending on the labeling line). In this work, samples that are printed with

flexographic printing with solvent-based dyes and UV dyes will be analyzed. Samples

will be analyzed on two types of polymeric materials (polypropylene and poly (vinyl

chloride)). The samples will treat at high temperature in the drier and it will be simulaor

for a tunnel for labeling. Samples will be exposed to high temperatures, depending on

the temperature of the printing substrate or polymeric material. Samples on

polypropylene will be exposed to temperatures of 120˚ and 125˚C, and samples on poly

(vinyl chloride) material at a temperature of 70˚C and 75˚C in the same duration of 5

minutes. The aim of this work is to determine the 90%, 70% and 20% rastertonic

deviation of contrasts after treatment with high temperature based on

spectrophotometric measurements and Euclidean difference in color.

• Ključne riječi: fleksografski tisak; stezljiv film; etiketiranje; boja na bazi otapala; UV sušeće boje; polipropilen; poli(vinil-klorid)
• Ključne riječi (engleski): flexographic printing; shrink sleeve; labeling; solvent-based color; UVdyeing; polypropylene; polyvinyl chloride
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:216:882009
• Studijski program: Naziv: Grafička tehnologija; smjerovi: Tehničko-tehnološki, Dizajn grafičkih proizvoda; Smjer: Tehničko-tehnološki; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra inženjer/inženjerka grafičke tehnologije (univ. mag. ing. techn. graph.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2024-04-18 22:25:18